Fe3+/SeO42- dual doped nano hydroxyapatite: A novel material for biomedical applications


ALSHEMARY A. Z. G. , PAZARÇEVİREN A. E. , TEZCANER A., EVİS Z.

JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS, cilt.106, ss.340-352, 2018 (SCI İndekslerine Giren Dergi) identifier identifier identifier

  • Cilt numarası: 106 Konu: 1
  • Basım Tarihi: 2018
  • Doi Numarası: 10.1002/jbm.b.33838
  • Dergi Adı: JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS
  • Sayfa Sayıları: ss.340-352

Özet

Dual ions substituted hydroxyapatite (HA) received attention from scientists and researchers in the biomedical field owing to their excellent biological properties. This paper presents a novel biomaterial, which holds potential for bone tissue applications. Herein, we have successfully incorporated ferric (Fe3+)/selenate ( SeO42-) ions into the HA structure (Ca10-x-yFey(PO4)(6-x)(SeO4)(x)(OH)(2-x-y)O-y) (Fe-SeHA) through a microwave refluxing process. The Fe-SeHA materials were characterized by X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, and field emission scanning electron microscopy (FESEM). XRD and FTIR analyses revealed that Fe-SeHA samples were phase pure at 900 degrees C. FESEM images showed that formation of rod-like shaped particles was inhibited dramatically with increasing Fe3+ amount. The Vickers hardness (HV) test showed that hardness values increased with increasing Fe3+ concentrations. Optical spectra of Fe-SeHA materials contained broadband over (200-600) nm. In vitro degradation and bioactivity tests were conducted in simulated body fluid (SBF). The incorporation of Fe3+/ SeO42- ions into the HA structure resulted in a remarkably higher degradation rate along with intense growth of apatite granules on the surface of the Fe-SeHA discs with Ca/P ratio of 1.35-1.47. In vitro protein adsorption assay was conducted in fetal bovine serum (FBS) and it was observed that the adsorption of serum proteins on Fe-SeHA samples significantly increased with increasing Fe3+ concentration. In vitro cytotoxicity tests were performed with human fetal osteoblast (hFOB) cell line and the results demonstrated that hFOB cells attached and proliferated faster on the Fe-SeHA materials compared to pure HA showing that Fe-SeHA materials were cytocompatible. ALP activity and intracellular calcium of hFOB cells on 1Fe-SeHA discs were statistically higher than pure HA, suggesting that presence of Fe3+ ion supported osteogenic differentiation of hFOB cells. Our results suggest that 1Fe-SeHA (0.2M Fe3+/0.5MSeO42- co-doped HA) material could be considered as a promising candidate material for orthopedic applications. (c) 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 340-352, 2018.