BIORESOURCES, cilt.5, ss.1473-1483, 2010 (SCI İndekslerine Giren Dergi)
The bending moment capacity was studied under the diagonal tensile and compression loadings of miter corner joints with dovetail fitting in frames made with medium density fiberboard (MDF). The influence of the type of adhesive in the joints with dovetail fitting on bending moment capacity under diagonal tensile and compression loading were considered, and the joints without adhesive were compared. A total of 80 each miter frame corner joint specimens with dovetail fitting were made. Polyvinyl acetate (PVAc), polyurethane (PU), and cyanoacrylate (CA) adhesives were used, and 20 specimens were prepared without adhesive (WA) with dovetail fitting. MDF was used as a frame material, as in normal practice. The specimens were subjected to diagonal tensile and compression loadings in accordance with ASTM-D 143-94. The data were analyzed statistically. The highest bending moment capacity under diagonal tensile loading (46.09 Nm) was obtained in the specimens bonded with CA adhesive and the highest bending moment capacity under diagonal compression loading (72.04 Nm) was obtained in the specimens glued with PVAc adhesive. Other than this, since there is no difference between these and the unbonded joints, the PU adhesive was not effective in increasing the bending moment capacity under diagonal tensile loading, and the PU and CA adhesives were not effective in increasing the bending moment capacity under diagonal compression loadings.